How to solve common defects in mold processing

Update:16-11-2020
Summary:

In the process of mold processing, what annoys you most […]

In the process of mold processing, what annoys you most is some common defects, these defects will directly lead to the performance of the workpiece, and even make the workpiece unable to be used here, so we must try to avoid some defects when we are processing the mold , Here are seven magic weapons for this problem.

1. Reasonably select and dress the grinding wheel. The white corundum grinding wheel is better. Its performance is hard and brittle, and it is easy to produce new cutting edges. Therefore, the cutting force is small, the grinding heat is small, and the medium grain size is used, such as 46~60 mesh is better. In the hardness of the grinding wheel, medium soft and soft (ZR1, ZR2 and R1, R2) are used, that is, coarse-grained, low-hardness grinding wheels. Good self-excitation can reduce cutting heat. It is very important to choose an appropriate grinding wheel during fine grinding. For the high vanadium and high molybdenum condition of the mold steel, it is more suitable to choose GD single crystal corundum grinding wheel. When processing hard alloys and materials with high quenching hardness, organic binder diamond is preferred. The grinding wheel, organic binder grinding wheel has good self-grindability, and the roughness of the ground workpiece can reach Ra0.2μm. In recent years, with the application of new materials, CBN (cubic boron nitride) grinding wheels have shown very good processing results. The effect is better than other types of grinding wheels for finishing on CNC forming grinders, coordinate grinders, and CNC internal and external cylindrical grinders. In the grinding process, attention should be paid to dressing the grinding wheel in time to keep the grinding wheel sharp. When the grinding wheel is passivated, it will rub and squeeze on the surface of the workpiece, causing burns on the surface of the workpiece and reducing its strength.

2. Reasonably use cooling lubricating fluid, play the three roles of cooling, washing and lubrication, keep cooling and lubrication clean, so as to control the grinding heat within the allowable range to prevent thermal deformation of the workpiece. Improve the cooling conditions during grinding, such as using oil-immersed grinding wheels or internal cooling grinding wheels. The cutting fluid is introduced into the center of the grinding wheel, and the cutting fluid can directly enter the grinding area to exert effective cooling and prevent burns on the surface of the workpiece.

3. Reduce the quenching stress after heat treatment to a minimum, because the quenching stress and the net-like carbonized structure will easily cause cracks in the workpiece due to the phase change of the structure under the action of the grinding force. For high-precision molds, in order to eliminate the residual stress of grinding, low temperature aging treatment should be carried out after grinding to improve toughness.

 

 

4. To eliminate the grinding stress, the mold can be immersed in a salt bath at 260~315℃ for 1.5min, and then cooled in 30℃ oil, so that the hardness can be reduced by 1HRC, and the residual stress can be reduced by 40%~65%.

5. For precision grinding of precision molds with dimensional tolerances within 0.01mm, attention should be paid to the influence of ambient temperature and constant temperature grinding is required. It can be seen from the calculation that the temperature difference of 300mm long steel parts is about 10.8μm when the temperature difference is 3℃, (10.8=1.2×3×3, the deformation amount per 100mm is 1.2μm/℃), and each finishing process needs to be fully considered The influence of this factor.

6. Electrolytic grinding is used to improve mold manufacturing accuracy and surface quality. During electrolytic grinding, the grinding wheel scrapes off the oxide film: instead of grinding the metal, the grinding force is small, the grinding heat is also small, and there will be no grinding burrs, cracks, burns, etc. The general surface roughness can be better than Ra0 .16μm; In addition, the wear of the grinding wheel is small, such as the grinding of cemented carbide. The wear of the silicon carbide grinding wheel is about 400% to 600% of the weight of the cemented carbide. When electrolytic grinding is used, the wear of the grinding wheel The amount is only 50%~* of the hard alloy grinding amount.

7. Reasonably choose the amount of grinding, and use the fine grinding method with small radial feed or even fine grinding. If the radial feed rate and grinding wheel speed are appropriately reduced, and the axial feed rate is increased, the contact area between the grinding wheel and the workpiece is reduced, and the heat dissipation conditions are improved, thereby effectively controlling the increase in surface temperature.